基本解释：初晶相
汉语字典(www.zxzidian.com)行业英语频道为您提供初晶相的英文是primary,phase,primary crystalline phase，primary,phase,primary crystalline phase的意思，primary,phase,primary crystalline phase是什么意思等内容，如果您正在查询primary,phase,primary crystalline phase缩写的全称、翻译、解释等信息，本页内容可供您参考
Effect of NaCl and LiF on liquidus temperature of molten cryolite-based aluminum electrolyte;NaCl和LiF的添加对铝电解质初晶温度影响的研究
Study on new device for testing liquidus temperature of aluminium electrolyte and mathematical model of liquidus temperature;铝电解质初晶温度测定装置及初晶点数模的研究
Study on direct determination of liquidus temperature of aluminium electrolyte;直接测定铝电解质初晶温度的研究
Control of the size of primary silicon in wrought Al-Si alloy;Al-Si系变形铝合金初晶硅尺寸的控制
Morphologies of primary silicon particles have significant influences on properties of hypereutectic Al-Si alloys, therefore the nucleation and growth mechanism and morphologies evolution mechanism of primary silicon particle have been widely investigated and become a major issue.初晶硅形态对高硅铝合金性能具有重要影响,其形核长大机制、形态演化机制是高硅铝合金的主要研究内容之一;尽管已有诸如变质剂处理、半固态搅拌、快速凝固、电脉冲处理等可改善初晶硅形貌的方法,但目前要完全实现控制初晶硅形态并使之球化,使用现有工艺较为困难。
The influences of trace addition of Na, Sr, or P on the nucleation and growth of primary silicon in Al22%Si alloy fabricated by high pure aluminum and silicon, in which the primary silicon mainly appeared in five petal starshaped morphology, were studied.在高纯原料配制的、以五瓣星状初晶硅形态为主的Ａｌ－２２％Ｓｉ高硅过共晶合金中加入少量的Ｎａ、Ｓｒ、Ｐ变质或细化元素，考察了它们对初晶硅形态的影响。
Effects of P Modification on Primary Si in Hypereutectic Al-Si Die Casting Alloy with Different Cooling Rates;P变质对不同冷速下过共晶压铸铝合金初晶Si的影响
Effects of Magnetic Field and Modification on Primary Si Morphology and Distribution;磁场和变质处理对初晶Si形状和分布的影响
Strong magnetic field method was adopted to solve the problems,such as the loss of efficiency after re-melt,the short effective time after Na modification,and the primary Si distributed unevenly after P modification.为解决Al-Si合金存在的Na变质重熔失效和有效时间短及P变质处理后初晶Si偏聚问题,利用施加强磁场的方法,分别对亚共晶Al-6%Si合金和共晶Al-12。
Influence of rare earth and Ni content on the primary crystallization of Al-Gd-Er-Ni metallic glass;稀土和镍含量对Al-Gd-Er-Ni金属玻璃初晶化的影响
The influence of Be replacement for Al on the glass forming ability(GFA)and primary crystallization of Al85Gd7Ni8alloy was investigated.研究了Be部分替代Al对Al85Gd7Ni8合金的玻璃形成能力和初晶化的影响。
The quantity of primary Si increases obviously and its average grain size decreases to about 35 μm.1%时即能达到理想的变质效果,使其初晶硅颗粒明显增多,平均颗粒尺寸下降到35!m左右;最佳变质温度为825℃左右;变质效果长效稳定,有着广阔的应用前景。
The primary Si formed in the melt are gradually changed from elongated platelets to polyhedral shapes.试验结果表明 :机械搅拌使初晶硅在剪切力作用下发生弯曲和破碎 ,并相互碰撞、集聚、合并长大 ,由板片状向多面体形转变 ;在固液两相区进行变温机械搅拌 ,冷却速度对初晶硅的颗粒直径有着重要的影响 ,随着冷却速度的增大 ,初晶硅的颗粒直径减小 ,当冷却速度为 5℃ / min时 ,初晶硅的颗粒直径小于 45μm,同时出现近球形的α相 ,获得了非常理想的半固态组
In this study, a novel Al-Si-P master alloy has been successfully prepared to modify and refine primary Si in eutectic and hypereutectic Al-Si alloys.该中间合金含有大量AlP颗粒,加入到共晶和过共晶Al-Si合金中后,分别起到促进初晶硅析出和细化初晶硅的作用。